- Question
Chrome magnesite brick is not used for lining the
Options- A. hearth of soaking pits.
- B. bottom hearth of reheating furnace.
- C. coke oven regenerator.
- D. burning zone of limestone rotary kilns.
- Correct Answer
- coke oven regenerator.
- 1. Rate of slag attack on refractories increases with rise in temperature due to the
Options- A. decreased viscosity of slag.
- B. increased thermal conductivity of brick.
- C. oxidising condition in the furnace.
- D. none of these. Discuss
- 2. Semi-silica bricks compared to silica bricks have
Options- A. less fusion point.
- B. better spalling resistance.
- C. both (a) and (b).
- D. neither (a) not (b). Discuss
- 3. Use of higher percentage of lime for bonding silica bricks, reduces their
Options- A. strength
- B. abrasion resistance
- C. both (a) & (b)
- D. neither (a) nor (b) Discuss
- 4. Upper portion of hot metal mixer are lined with mullite bricks, which helps in resisting the
Options- A. washing action of metal.
- B. corrosion by layer of slag.
- C. both (a) & (b).
- D. neither (a) nor (b). Discuss
- 5. The maximum linear expansion of silica bricks during firing is about __________ percent.
Options- A. 0.5
- B. 1
- C. 2
- D. 3.5 Discuss
- 6. To resist spalling tendency, a refractory should have
Options- A. greater diffusivity.
- B. low specific heat.
- C. low thermal co-efficient of expansion.
- D. all (a), (b) and (c). Discuss
- 7. Grog addition in fireclay during brick manufacture is done to
Options- A. reduce its shrinkage on heating.
- B. impart greater spalling resistance.
- C. enhance the strength of fired refractories.
- D. all (a), (b) and (c). Discuss
- 8. Roof of a basic open hearth furnace is lined with __________ bricks.
Options- A. silica
- B. fireclay
- C. dolomite
- D. magnesite Discuss
- 9. Which property is important for bricks used in the combustion chamber & dome of blast furnace stoves?
Options- A. High refractoriness.
- B. High resistance to spalling.
- C. High strength and density.
- D. All (a), (b) and (c). Discuss
- 10. Spalling tendency of refractories is reduced by increasing its
Options- A. porosity
- B. specific gravity
- C. thermal conductivity
- D. strength Discuss
Refractory Technology problems
Search Results
Correct Answer: decreased viscosity of slag.
Correct Answer: both (a) and (b).
Correct Answer: both (a) & (b)
Correct Answer: washing action of metal.
Correct Answer: 3.5
Correct Answer: all (a), (b) and (c).
Correct Answer: all (a), (b) and (c).
Correct Answer: silica
Correct Answer: High refractoriness.
Correct Answer: porosity