Discussion
Home ‣ Chemical Engineering ‣ Refractory Technology Comments
- Question
The maximum linear expansion of silica bricks during firing is about __________ percent.
Options- A. 0.5
- B. 1
- C. 2
- D. 3.5
- Correct Answer
- 3.5
- 1. Dilatometer is used for the determination of __________ of refractories.
Options- A. modulus of rupture
- B. permanent linear change
- C. resistance to CO attack
- D. RUL Discuss
- 2. Graphite or carbon refractories
Options- A. exihibit wetting characteristics.
- B. should be used in neutral or reducing atmosphere.
- C. exhibit high shrinkage on thermal treatment.
- D. are not resistant to corrosion by slag. Discuss
- 3. Mullite is chemically represented by
Options- A. Al2O3 . 2SiO2
- B. 3Al2O3 . 2SiO2
- C. Al2O3 . SiO2
- D. 2Al2O3 . 3SiO2 Discuss
- 4. Maximum apparent porosity of magnesite bricks is about __________ percent.
Options- A. 8
- B. 24
- C. 44
- D. 58 Discuss
- 5. SiO2 percentage in firebrick is about
Options- A. 35-40
- B. 55-60
- C. 80-85
- D. >94 Discuss
- 6. Upper portion of hot metal mixer are lined with mullite bricks, which helps in resisting the
Options- A. washing action of metal.
- B. corrosion by layer of slag.
- C. both (a) & (b).
- D. neither (a) nor (b). Discuss
- 7. Use of higher percentage of lime for bonding silica bricks, reduces their
Options- A. strength
- B. abrasion resistance
- C. both (a) & (b)
- D. neither (a) nor (b) Discuss
- 8. Semi-silica bricks compared to silica bricks have
Options- A. less fusion point.
- B. better spalling resistance.
- C. both (a) and (b).
- D. neither (a) not (b). Discuss
- 9. Rate of slag attack on refractories increases with rise in temperature due to the
Options- A. decreased viscosity of slag.
- B. increased thermal conductivity of brick.
- C. oxidising condition in the furnace.
- D. none of these. Discuss
- 10. Chrome magnesite brick is not used for lining the
Options- A. hearth of soaking pits.
- B. bottom hearth of reheating furnace.
- C. coke oven regenerator.
- D. burning zone of limestone rotary kilns. Discuss
Refractory Technology problems
Search Results
Correct Answer: permanent linear change
Correct Answer: should be used in neutral or reducing atmosphere.
Correct Answer: 3Al2O3 . 2SiO2
Correct Answer: 24
Correct Answer: 55-60
Correct Answer: washing action of metal.
Correct Answer: both (a) & (b)
Correct Answer: both (a) and (b).
Correct Answer: decreased viscosity of slag.
Correct Answer: coke oven regenerator.