In panel test for spalling resistance, the average face temperature of panel assembly is maintained at __________ °C for 24 hours.
Options- A. 700
- B. 1000
- C. 1600
- D. 2000
- Correct Answer
- 1600
- 1. Rotary kilns meant for calcination of limestone are lined with chrome magnesite in __________ zone.
Options- A. preheating
- B. cooling
- C. burning
- D. all Discuss
- 2. Fireclay refractories
Options- A. are not resistant to the action of basic slags.
- B. combine with salts (e.g. chlorides sulphates etc.) & bases (e.g. lime, magnesia etc.) forming fusible aluminates silicates etc.
- C. shrink during firing
- D. all (a), (b) and (c) Discuss
- 3. Refractoriness under loads (RUL) is quite close to the fusion temperature (PCE) for __________ bricks.
Options- A. fireclay
- B. silica
- C. dolomite
- D. very low alumina Discuss
- 4. Refractory bricks having lower porosity have
Options- A. high insulating properties
- B. low heat capacity
- C. low thermal conductivity
- D. greater strength Discuss
- 5. Crushing strength of a refractory
Options- A. increases with rise in service temperature.
- B. decreases with rise in service temperature.
- C. is unaffected with change in service temperature.
- D. decreases with increase in porosity. Discuss
- 6. Hot blast main (carrying air at 1000°C) in blast furnace are lined with __________ bricks.
Options- A. silica
- B. fireclay
- C. magnesite
- D. zirconia Discuss
- 7. Ceramic recuperators used for waste heat recovery from high temperature flue gas going out of the furnace is made of
Options- A. fireclay
- B. silicon carbide
- C. corrundum
- D. siliceous fireclay Discuss
- 8. Pick out the wrong statement.
Options- A. Insulating refractories used in place of regular refractory bricks are usually called light weight refractories, and they have similar composition as heavy bricks.
- B. Graphite refractories are also called plumbago refractories.
- C. Superduty fireclay bricks correspond to a pyrometric cone equivalent of 26-28.
- D. Calcined magnesite is also called dead burnt magnesite. Discuss
- 9. Dolomite bricks have good resistance to attack by
Options- A. molten steel
- B. iron oxide
- C. lime slag
- D. none of these Discuss
- 10. Magnesite chrome refractories
Options- A. have better spalling resistance than chrome magnesite refractories.
- B. have very low thermal co-efficient of expansion.
- C. are not at all resistant to the corrosive action of iron oxide.
- D. have very low (50 kg/cm2 ) cold crushing strength (C.C.S.), and can not be used in metalcase form. Discuss
Refractory Technology problems
Search Results
Correct Answer: burning
Correct Answer: all (a), (b) and (c)
Correct Answer: silica
Correct Answer: greater strength
Correct Answer: decreases with rise in service temperature.
Correct Answer: fireclay
Correct Answer: silicon carbide
Correct Answer: Superduty fireclay bricks correspond to a pyrometric cone equivalent of 26-28.
Correct Answer: molten steel
Correct Answer: have better spalling resistance than chrome magnesite refractories.